Monocrystalline Solar Cells Alum Paste Uniform / Thick BSF Forming

Hunan LEED Electronic Ink Co., Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Hunan LEED Electronic Ink Co., Ltd
City: Zhuzhou
Province/State: Hunan
Country/Region: China
Tel: 86-731-22976365

Monocrystalline Solar Cells Alum Paste Uniform / Thick BSF Forming

Brand Name : LEED-INK
Model Number : BL01A
Certification : CE, SGS, RoHS, ISO9001, ISO14001
Place of Origin : China
MOQ : 1KG
Price : Negoatiable
Payment Terms : L/C, T/T, Western Union
Supply Ability : 300000KG per month
Delivery Time : Within 7 days after payment confirm
Packaging Details : 1KG/Plastic Jar, 6 Jars/ Carton. Carton size: 39*26*17cm. G.W.:7.5KG/ Carton.
Solid Content (%) : 70-80
Viscosity (Pa.S) : 40-120
Wet Deposit (g/pcs) (156*156) : 1.24-1.4
Bow : Monocrystal silicon: ≤2.0mm; Polysilicon:≤1.8mm
Eff. : Monocrystal silicon: ≥19.50; Polysilicon:≥18.50
Contact Now

Good Adhesion Solar Cell Paste for Monocrystalline and Multicrystalline

Silicon Solar Cells


Description

BL01A series products was specially developed to apply with higher firing peak temperature process. Innovative technologies and materials allow BL01A to provide efficiency gain to solar cells while keeping up all the other essential characteristics and prove to be standard for the materials manufactured.


Application

A typical aluminum paste contains metal powders, glasses and additives mixed in an organic medium. The Al Paste variables such as metal powder, glass chemistry and additives have an influence on electrical performance, wafer bowing and solar cell adhesion. Increased electrical efficiency is typically not associated with Aluminum Paste, but many customers have seen up to 0.1% efficiency increase with our paste due to improved back-surface-field (BSF) strength.


Benefits

Al paste designed for crystalline silicon wafer

  • Retaining product lines for Pb contained & Pb free
  • High Voc let it have improved efficiency
  • Uniform and thick BSF forming
  • Excellent physical properties (BOW / EVA PEEL FORCE / HOT WATER TEST)

Typical Properties


TestProperties
Solid Content (%)70-80

Viscosity (Pa.S)

(NDJ-8S, #4, 25±0.5℃)

40-120
Fineness(μm)≤22

Recommended

Drying Conditions

Chain fast burning furnace:

280℃-350℃/25-50sec;

Rotating drying furnace:

180℃-250℃/8-15min

Practical

Peak Temperature

770-830℃

Wet Deposit (g/pcs)

(156*156)

1.24-1.4

Resistivity (mΩ/sq)

(Fired Thickness)

≤30

Cell Warpage

(156 mono/polycrystal

silicon,180μm)

Monocrystal silicon: ≤2.0mm;

Polysilicon:≤1.8mm

Adhesion (N) (Single side EVA tape)>20
Photoelectrical Conversion Efficiency(%)

Monocrystal silicon: ≥19.50;

Polysilicon:≥18.50

Shelf LifeSix Months from Date of Shipment

Why Choose Us?

1. High-quality products and the most reasonable price.

2. Professional R&D team technical service.

3. Customiszed production for different package.

4. To follow orders and arrange shipping in time, providing complete documents for Customs clearance according to different export policies in different countries.


Product Tags:

silver thermal paste

      

aluminium solder paste

      
China Customized Inflatable Bumper Ball Game Bubble Adult Grass CE supplier

Monocrystalline Solar Cells Alum Paste Uniform / Thick BSF Forming Images

Inquiry Cart 0
Send your message to this supplier
 
From:
Enter your email please.
To: Hunan LEED Electronic Ink Co., Ltd
Subject:
Message:
Characters Remaining: (0/3000)